Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Terblend® N NM-12 - (ABS+PA6) - INEOS Styrolution

Check here, which other Terblend N datasheets, application examples or technical articles are available in Material Data Center

加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

Terblend® N NM-12 is an ABS/PA blend combining high impact strength and rigidity with a excellent processability and surface appearance.

加工/物理特性	干 / 已调节	单位	Test Standard
ISO数据
熔体体积流动速度, MVR	34 / *	cm³/10min	ISO 1133
温度	240 / *	°C	-
载荷	10 / *	kg	-
模塑收缩率, 平行	0.7 / *	%	ISO 294-4, 2577
模塑收缩率, 垂直	0.8 / *	%	ISO 294-4, 2577
熔体密度	928	kg/m³	-
熔体	0.156	W/(m K)	-
熔体的比热	2410	J/(kg K)	-
喷射温度	90	°C	-

机械性能	干 / 已调节	单位	Test Standard
ISO数据
拉伸模量	2200 / 1600	MPa	ISO 527
屈服应力	50 / 45	MPa	ISO 527
屈服伸长率	3.2 / 5	%	ISO 527
名义断裂伸长率	20 / >50	%	ISO 527
无缺口简支梁冲击强度, +23°C	N / -	kJ/m²	ISO 179/1eU
简支梁缺口冲击强度, +23°C	17 / -	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度, -30°C	9 / -	kJ/m²	ISO 179/1eA

热性能	干 / 已调节	单位	Test Standard
ISO数据
热变形温度, 1.80 MPa	66 / *	°C	ISO 75-1/-2
热变形温度, 0.45 MPa	88 / *	°C	ISO 75-1/-2
维卡软化温度, B	105 / *	°C	ISO 306
线性热膨胀系数, 平行	90 / *	E-6/K	ISO 11359-1/-2
1.5mm名义厚度时的燃烧性	HB / *	class	IEC 60695-11-10
测试用试样的厚度	1.6 / *	mm	-
厚度为h时的燃烧性	HB / *	class	IEC 60695-11-10
测试用试样的厚度	3.2 / *	mm	-

电性能	干 / 已调节	单位	Test Standard
ISO数据
相对介电常数., 100Hz	3.3 / -	-	IEC 62631-2-1
相对介电常数., 1MHz	2.9 / 3.3	-	IEC 62631-2-1
介质损耗因子, 1MHz	150 / 550	E-4	IEC 62631-2-1
体积电阻率	>1E13 / 1E11	Ohm*m	IEC 62631-3-1
表面电阻率	* / 1E14	Ohm	IEC 62631-3-2
相对漏电起痕指数	600 / 600	-	IEC 60112

其它性能	干 / 已调节	单位	Test Standard
吸湿性	1.2 / *	%	类似ISO 62
密度	1070 / -	kg/m³	ISO 1183

函数

典型数据

加工方法

注塑

供货形式

粒料

特殊性能

防静电的

地区供应

北美, 欧洲, 亚太, 中南美洲, 中东/非洲

其他信息

注塑成型

PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
injection molding, Melt temperature, range: 240 - 270 °C
injection molding, Melt temperature, recommended: 260 °C
injection molding, Mold temperature, range: 40 - 80 °C
injection molding, Mold temperature, recommended: 60 °C

耐化学性

酸类
	醋酸 (5g/100g) (23°C)
	柠檬酸溶液 (10g/100g) (23°C)
	乳酸 (10g/100g) (23°C)
	盐酸 (36g/100g) (23°C)
	硝酸 (40g/100g) (23°C)
	硫酸 (38g/100g) (23°C)
	硫酸 (5g/100g) (23°C)
	铬酸溶液 (40g/100g) (23°C)
碱类
	氢氧化钠溶液 (35g/100g) (23°C)
	氢氧化钠溶液 (1g/100g) (23°C)
醇类
	甲醇 (23°C)
	乙醇 (23°C)
碳氢化合物
	异辛烷 (23°C)
酮类
	丙酮 (23°C)
醚类
	(二)乙醚 (23°C)
标准燃油
	柴油(优先使用F类ISO 1817液体) (23°C)
盐溶液
	氯化钠溶液(10g/100g) (23°C)
	次氯化钠溶液 (10g/100g) (23°C)
	碳酸钠溶液 (20g/100g) (23°C)
	碳酸钠溶液 (2g/100g) (23°C)
	氯化锌溶液 (50g/100g) (23°C)
其它
	乙酸乙酯 (23°C)
	过氧化氢 (23°C)
	1g/100g 基苯氧- 聚环氧乙烷乙烯水溶液 (23°C)
	水 (23°C)

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com